CX EP SELF LEVEL 03

CX EP SELF LEVEL 03 chemical and acid resistant epoxy self leveling for decorative floor. CX EP SELF LEVEL 03 is a 4-component solvent free epoxy resin based flooring system applied @ 1 mm thickness.

Uses: As a high build coating or self-leveling floor topping for: Automobile & Engineering units Electronics / electrical / Plastics industry Food processing industry Chemical / pharmaceutical industry Textile & paper Industries Power stations Schools & Institutions Laboratories and rooms subject to radiation Clean rooms, exhibition halls and showroom Wet and dry process areas i.e. beverage industry, bottling plants, Dairies, meat processing plant etc. Warehouses, logistics, loading bays and ramps Aviation Hangars.

Inquiry
Wholesale Bucket Supplier

Download Brochure to view our product

Advantages
right

Self-leveling

Excellent self-leveling properties

right

Abrasion

Good abrasion resistance

right

Durability

High durability

right

Solvent

Solvent free

right

Waterproof

Waterproof

right

Mechanical

High mechanical properties

right

Chemical

Good chemical resistance

right

Coloured

Coloured & excellent gloss

right

Easily cleaned

Easily cleaned & maintained

Mechanical Properties
Compressive Strength : 60 N/mm2
Flexural Resistance :31 N/mm2
Tensile Resistance : 23 N/mm2
Abrasion Resistance: 50 mg weight loss (Taber Abraser), 28 days
Adhesion : >1.5 N/mm2
Shore D Hardness : 80
Application

Instructions

  • Consumption / Dosage : Self smoothing topcoat CX EP SELF LEVEL 03 ~ 1.5 to 1.6 kg/m2/mm 1 set of CX EP SELF LEVEL 03 will cover 10 - 11 sqm @ 1mm thickness.
  • Substrate Quality : The concrete substrate must be sound and of sufficient compressive Strength (minimum 25 N/mm2 ) with a minimum pull off strength of 1.5 N/mm2 . The substrate must be free of all contaminants such as oil, grease, coatings and surface treatments etc. If in doubt, apply a test area first.
  • Substrate Preparation : Concrete substrates must be prepared mechanically using abrasive blast cleaning or scarifying equipment to remove cement laitance and achieve an open textured surface. Weak concrete must be removed and surface defects such as blow holes and voids must be fully exposed. Repairs to the substrate, filling of blowholes/voids and surface levelling must be carried out using appropriate Chimique Sol products. High spots can be removed by grinding. All dust & loose material must be completely removed from all surfaces before application of the product, preferably by brush or vacuum.
  • Substrate Temperature : +8°C min. / +40°C max
  • Mixing Stir : Component A first for approx. 15 seconds. Add component B, and mix for approx. 30 seconds with low speed mixer. While mixing, add simultaneously but slowly (DON’T DUMP!) component C (colour paste EPI) and Component D (filler) within 30 seconds. Further mix for 1 minute until the mixture is homogeneous and the pigment is uniformly dispersed.
  • Application Process & Tools : Prior to application, confirm substrate moisture content. If > 4% moisture content Make sure that a continuous, pore free coat covers the substrate. Apply CX EP SELF LEVEL 03 by brush, roller or trowel.

Waiting Time

Substrate temperature Minimum Maximum
+25°C 12 hours2 hours Light sanding required after maximum time.

Potlife

Temperatures Time
+25°C ~ 15minutes

Timing of Application

  • The timing of application CX HARDTOP 330 special is important and critical. If applied too early, bleed or excess water will wash away the cementitious content of the products, thereby making them ineffective. Also denser aggregates sink into the concrete. If the application of CX HARDTOP 330 special is done too late, there will not be sufficient water/moisture to absorb the material into the concrete. Material forcibly applied and trowelled thus, will cause cracks on the surface later, as there is no water/ moisture to hydrate the product.
  • Bay edges : CHWhile applying CX HARDTOP 330 special at the edges of the concrete floor or, at the end of bays, extra precaution should be taken by way of sprinkling more material and finishing it smoothly with a steel trowel. This isan additional protection particularly to bay edges where the reaction due to heavy or impact is felt more.
  • Curing : ests have shown that proper curing of concrete floors treated with products such as CX HARDTOP 330 special is essential to ensure the physical properties of the floor. The most efficient method of curing by using CB SUPERCURE WB, curing membrane which conforms to ASTM and DOE specifications
  • Ready To Use : CX HARDTOP 330 special is supplied ready to use on site. Cement or aggregates should never be added to CX HARDTOP 330 special
  • Colored Floors : When a colored floor is required, it is strongly recommended that a job site trial area is laid.
  • Surface Treatment : Penetration type surface treatments are recommended to give low porosity and dust proof property.
Chemax Self Level Application
Newer CX BLACK COAT 220
Back to list
Older CX MT HARDTOP 331

Related Projects

  • Accelerators & Concrete Block Admixture
  • Concrete Admixture

CX Fast Set P+

  • Concrete Admixture
  • High Range Water Reducing Admixture (Super Plasticizer)

CHEMAX GROUT A01

  • Concrete Admixture
  • High Range Water Reducing Admixture (Super Plasticizer)

CX AIR ENTRAINING